YOOGU reinforced epoxy iron oxide red antirust paint, is a kind of micaceous iron oxide as the main antirust pigment heavy-duty epoxy antirust paint, by epoxy resin, micaceous iron oxide, antirust pigment, with various kinds of imported auxiliaries carefully developed and become. The film has good salt tolerance, moisture resistance, water resistance and good adhesion and physical mechanical properties. The film has excellent durability, wear resistance and moisture resistance because it contains mica oxide. Epoxy mica is not easy to be damaged, easy to handle, can be applied in the factory, after the construction site, and the surface treatment requirements are very low. This kind of anti-corrosion thick slurry type primer, intermediate paint or surface paint can provide a strong protective effect in the high performance coating package.

The construction is convenient and quick, simple, can be directly in new metal or old metal material surface spray;
The anti-corrosion materials are of high quality industrial anticorrosive paint. They are green and environmental protection coatings, which are excellent in corrosion resistance, low temperature and flexible.
With strong adhesion, it has good adhesion to other high performance paint.
Excellent durability resistance to high temperature environment;
Excellent corrosion resistance. Excellent wear resistance and adhesion;
Easy to construct, can be brushed, rolled and sprayed;
Do not add lead, chromium, mercury and other harmful heavy metals.

Epoxy micaceous iron oxide coating is suitable for all kinds of metal material, caigang watts, aluminum, stainless steel, iron gate, stair), metal storage tanks, pipelines, steel structure metal stents, metal equipment, such as surface has been widely used throughout the area, is now the best metal roofing heavy-duty anticorrosion.

Construction method

1. This product YOOGU reinforced epoxy mica anti-rust paint needs to be matched with primer and topcoat for better effect. It can be applied by spraying, rolling or painting.

2. First remove the floating rust, dust, oil stains and garbage on the base surface, and repair and flatten the rust through parts.

3. On the cleaned base surface, brush or spray the functional automatic derusting primer together, the coating is uniform without exposed bottom, and the drying time is more than 8 hours.

4. Paint or spray YOOGU reinforced epoxy mica anti-rust intermediate paint together, the coating is uniform without exposed bottom, and the drying time is more than 8 hours.

5. Paint or spray YOOGU acrylic anti-corrosion topcoat together, the coating is uniform and no bottom, and it can be accepted after drying for more than 36 hours (adjustable surface color).

specifications
Surface treatment: the front coating should be completely dry and remove all the oil and grease from the paint film.
Mixing ratio: a single group of paint, open the package after sufficient stir to be used.
Limitations: the substrate should be higher than 3 ℃ above the dew point temperature. Relative humidity is not greater than 85%.
Coating method: airless spray: nozzle diameter: 0.2-0.4mm
Ejection pressure: 15 ~ 18MPa
Thinner XC108
Dilution: 0 ~ 5% (in paint weight gauge)
Air spray: nozzle diameter: 2.0 ~ 2.5mm
Air pressure: 0.3 ~ 0.4mpa
Tool cleaning: XC108
Coating: zinc rich epoxy primer, functional automatic rust primer, polyurethane high level paint, acrylic anticorrosion paint, etc.
Packing specification: 20 ~ 22kg can be canned (related to color).
Shelf life: 12 months.